How to make liquid plastic with your own hands? Manufacturing technology and scope of application

Plastic products are durable and do not require special maintenance conditions. To make them, liquid plastic is used for pouring, which is purchased in a store or made independently at home. Before starting work, you must familiarize yourself with the cooking technology and observe safety precautions.

We will advise you on any questions!

Plastic parts are widely used in all industries. The scope of human activity is also associated with the use of plastic, from building materials and household appliances to kitchen utensils. The most popular method of manufacturing various products is plastic injection molding technology. Modern equipment makes it possible to automate the production process and obtain products with excellent technical characteristics in a short time with minimal investment. Polymer products are recyclable and therefore are an environmentally friendly material.

Manufacturing using liquid plastics

The manufacturing process is carried out using liquid plastics and silicone molds. Now it is possible to produce plastic products in small batches at home:

• souvenirs;
• toys;
• costume jewelry;
• spare parts for auto tuning;
• spare parts for various mechanical devices;
• shoes;
• dishes

There are components for the manufacture of parts from thin-walled plastic, which can significantly expand the range of products and produce parts of any complexity. For example, mixing two components of the Axson FASTCAST F32 brand from a French manufacturer makes it possible to obtain a super-liquid plastic that flows into the smallest folds of the relief of the model’s shape. In addition, it is harmless to children and has no odor.

What is plastic injection molding

Large-scale and mass production of plastic parts involves a complex technological process of injecting molten plastic under high pressure into a prepared injection mold made of metal. The liquid mass evenly fills the volume and crystallizes, acquiring the required shape. Thanks to injection molding technology, it is possible to obtain high-quality products. To implement the method, complex, expensive equipment is used that provides high productivity. Almost half of the polymer parts are produced using this method. Thermoplastic granules, as well as thermosetting powders, are used as raw materials for the production process, giving the finished products the required physical and performance qualities. Thermoplastic components retain their parameters during recycling, while thermoset components undergo irreversible chemical reactions and form an infusible material.

The prepared polymer components are loaded into the hopper of the injection molding machine, in which they are melted and homogenized. Next, the mass is injected at speed, thanks to the pressure created, through special channels into the prepared form. The cavity quickly fills. After solidification, a casting is formed. The quality of polymer products depends on the injection speed. Worm-type plasticizers are the most popular. They are characterized by high productivity and better homogenization of the molten mass. Less popular piston type equipment. It provides the supply of molten polymer at high speed into the injection mold and provides the opportunity to obtain a marble effect in the case of preparing a mixture of multi-colored plastics. In production, the use of a separate method is allowed. It involves the preparation of the molten mass in a preplasticizer with a worm mechanism, and the dosing and injection of the viscous mass into the mold is carried out using piston-type equipment.

Raw materials, materials for injection molding of plastics

The raw materials for plastic injection are thermosetting powders, as well as granules of thermoplastics and thermoplastic elastomers. All materials have different mechanical and physical characteristics.

The advantage of thermoplastic materials is that they can be recycled after the molding process. Thermosetting materials in the process of molding a product are subject to chemical processes that lead to the transformation of raw materials into an infusible and insoluble material.

Applications of polymer injection molding

Using technology that involves plastic injection molding, it is possible to produce simple and complex plastic parts. There are no restrictions on the dimensions and number of products. This method is used in the automotive industry, electronics, chemical and many other industries. Using the plastic injection method, it is possible to quickly and with the required level of quality produce:

• different packaging, lids and different caps;
• a wide range of children's toys;
• housings and components for electronic equipment;
• components for medical equipment and other products.

Precautionary measures

Acetone is a very dangerous liquid that has an extremely negative effect on the human body. Therefore, it is allowed to make liquid plastic with your own hands only if the following precautions are strictly observed:

1. Before working with acetone, you must carefully study the instructions for its use. It is indicated on the container label.
2. Special sealed safety glasses should be used. They will protect your eyes in case of liquid drops and vapors. Working without them can cause serious eye injury.
3. Acetone is toxic, so it should only be used in a well-ventilated area. In this case, it is necessary to use respiratory protection.
4. This is a highly flammable product. Therefore, liquid plastic is made with your own hands away from sources of open fire. Smoking is strictly prohibited when performing work.
5. Residues of acetone must not be poured into the sewer system.
6. At the end of the process, as well as after pouring the finished plastic into molds, you must thoroughly wash your hands.

Advantages of this technology

For the production of large quantities of polymer products, plastic injection molding technology is characterized by the advantages of high casting accuracy. By injecting the molten mass at an increased speed, the mold is uniformly filled, including microscopic holes. The method is characterized by many advantages due to which it is popular:

• Possibility of producing products of any geometric shape and degree of complexity. Thin-walled parts are manufactured. The complexity of the design depends on the mold, which is highly detailed and takes into account all the bends and holes of the future product.
• There is no need for subsequent machining of parts. Some products that are complex in design may require minimal processing.
• Mass production of an unlimited number of plastic parts. The service life of metal molds is tens of years, so they are used for the manufacture of a huge number of polymer products.
• Quick payback when organizing the production of large batches of plastic products. At the same time, the cost of one product decreases without deterioration in quality as the number of copies produced increases. This dependence is explained by a one-time investment of funds at the preparatory stage for the release of a certain type of product.

Technology involving pressure casting has significant costs at the preparation stage, so its use is unprofitable for the manufacture of single products or small batches.

Mold making

Next, watch a video on how to make a mold for pouring plastic.

Polypropylene casting machine

The author of the OumeletsTV channel showed a self-made machine for home plastic molding. It's electric. The piston is manual. Thermostat for precise temperature control. The video shows his tests. For these purposes he will cast nylon or polyamide. There is another name - nylon. Chair crosspieces are usually made from nylon. The master found just such a thing, he crushed it. Before use, the mug must be dried at a temperature of up to 100 degrees. This must be done within 2-4 hours.

Load the granules into the machine. Let's set it to 250 degrees. This is the optimal temperature for polyamide casting. Let's wait until the required degrees are reached. Then we will install the piston. The machine has reached optimal mode, the indicator light is on. Now you need to wait 5 minutes for the plastic to completely warm up from the inside.

The polyamide has warmed up. We put it on the mold. We press in. We do pressure aging. It's obvious that he's flooded. Let's let it cool a little. Now let's disassemble the mold. Studied plastic product. As you can see, there is no shrinkage.

Staged production

The process, organized using injection molding technology, is carried out in stages. Complex work consists of preparatory operations and product formation.

Preparatory work includes 3D modeling of future products. In order to create a model, specialists analyze and study drawings, photographs and product descriptions. After creating a three-dimensional model using special software and approving it, the following operations are performed:

1. A prototype is made, which is a sample of the part being produced. In order to speed up the process, modern equipment (printers) that perform 3D printing is used. The manufactured prototype allows you to evaluate, test under extreme loads and test the finished product. If inaccuracies and defects are detected, changes are quickly made to the three-dimensional model until an ideal part is obtained that meets all requirements.
2. Molds are designed. At this stage, all the details (lines, bends, holes, etc.) are carefully worked out based on the approved 3D model.
3. Molds are made to be filled with the molten mass. For this purpose, the three-dimensional model is divided into parts. Each received element is manufactured separately. At the last stage, the parts are assembled into a form.
4. Casting of the first copy from plastic. It is carefully checked and tested. If inaccuracies are detected, the injection mold is modified.

Depending on the complexity of the products, preparation work may take several weeks or months. The quality of future polymer products depends on the completeness and accuracy of operations at this stage.

The product formation process involves:

1. Melting the components and feeding the melt into the mold.
2. Creation of pressure for the purpose of rapid filling and uniform distribution of the polymer mass over the mold.
3. Cooling the filled volume until the plastic has completely hardened. The time required for polymer crystallization depends on many parameters: the type of plastic used, melt viscosity, temperature in the mold, etc. For oversized parts, the cooling process lasts for several seconds.
4. Receiving the finished product. After complete cooling, the mold is separated to obtain the part.

The final cost of products is calculated individually for each type and depends on the design complexity of the product, the type of polymer material, the volume of the product batch and other factors.

Opportunities for a small business idea

This business idea makes it easy to create popular products with your own hands. Finished works can be sold through an online store. It is also possible to provide services or sell finished compounds to other manufacturers in other industries. The most important thing is that with all these wide possibilities of home business, the cost of components is more than affordable. The range of components is wide and allows you to select the necessary materials for creating forms or filling them. All that is required is a sample model from which the mold will be removed. This business idea is very attractive for a home business. It does not require a lot of costs, allows you to produce useful goods and captivates you with the creative production process.

Methods used for plastic injection molding

To implement the technology for producing products from molten polymers, injection molding machines (TPAs) are used, which are special injection molding units that differ in the location of injection units. The melt is injected vertically downwards or in a horizontal plane. According to the type of raw materials used, injection molding machines are classified, providing single-component or multi-component injection molding of plastics, performed in different ways.

Injection

This method is the most common. The required portion of the molten mass accumulates in the cylinder and is injected under pressure into the mold. Casting pressure is ensured at 200 MPa. The process of feeding the mass occurs in seconds. As a result, it is possible to produce parts with complex configurations. It is possible to obtain different wall thicknesses. Thermoplastics and thermosetting plastics can be used as raw materials. It is possible to use a multi-cavity injection mold. The volume of molten mass must exactly match the sprues.

Intrusive

Designed for casting thick-walled plastic products. This plastic injection method involves feeding molten material into a mold by rotating a worm gear. In order to compensate for the natural shrinkage formed after cooling the mass, the worm, with an axial movement, supplies the missing melt. When implementing this method, the amount of injected mass may exceed the volume required to cast the part. The casting pressure is insignificant, so the method is used to obtain products of simple shapes with limited nesting.

Injection-press

This plastic molding method allows the production of products characterized by a large pressing area. The pressure drop during the filling process causes different strength characteristics in the center and in the outer zones of the parts. The peculiarity of the technology is the formation of mass pressure not only through injection, but also through the use of a pressing mechanism of a moving unit. Therefore, forms are used that structurally provide for the movement of parts after they are connected.

Gas injection

IGL is a new method used for polymer processing. The essence of the technology is to melt raw materials and feed the mass through injection units in order to fill the mold by 80–95%. A gas mixture (carbon dioxide) is pumped through a special nipple using a compressor under a pressure of 80 MPa. It inflates the melt, filling all the depressions and increasing the thickness of the plastic. After the part is formed, the gas evaporates into a special receiver, and the required amount of molten mass is supplied to the mold to complete the manufacture of the product.

Gas injection molding provides the opportunity to save almost half of the expensive raw materials used, reduce the likelihood of defects, reduce production cycle time, and optimize the cost of tooling. The technology requires precise control of the LM, is characterized by a complex nozzle design and increased requirements for the injection system.

Multilayer

This method involves the use of two or three injection units for the process for the purpose of plasticizing a polymer characterized by certain properties. The result is multi-colored parts, the structure of which is made up of different types of polymer materials. Multilayer plastic injection molding is used to produce hybrid structures in which non-critical parts are made from recycled materials.

Sandwich casting

The technology provides for variable supply of molten polymer into the mold from different plasticizers. For this purpose, two injection modules are connected to a sprue with a switching mechanism, which uses a needle valve. A valve connects them to the mold in a specific sequence or simultaneously. From the first, a mass is injected under pressure to form the outer coating of the part being manufactured. The internal cavities are filled with polymer coming from the second unit. At the last stage, the first node is switched again to add melt.

Co-injection

In order to ensure this type of injection molding, nozzles made according to a special design in the form of a dividing head are used. This method is widely used to produce parts with more than two layers, completely or partially different in color.

Multi-component mold casting

The MCIM method provides the opportunity to organize the production of multi-colored products with a diverse design. In these parts, the central and peripheral parts are made of different polymer materials. When implementing this method, injection units operate in standard mode, and the configuration of the part is formed using a special mold structure. It structurally consists of two systems that are closed with the first and second nodes, and also includes movable inserts that are moved using pneumatic actuators. Each insert forms the structural elements of the part. The units operate in different modes (injection or intrusion) independently of each other. Thanks to this design feature, it is possible to form products of large sizes.

Rotary

This method is a type of plastic molding into complex shapes using a removable insert. After the central part of the part is formed (the first node works), the insert is removed. The molten mass from the second module enters the vacated volume. The production cycle is characterized by an additional operation involving the separation of the injection mold in order to remove or install the insert. This method has lower productivity.

Making plastic products and molds with your own hands

A business idea for organizing small-scale production of products from various injection molding materials at home. Thanks to innovative technologies, today in the production of plastic products it is possible to do without expensive automatic thermoplastic machines. Moreover, you can set up small-scale mini-production right on your desktop. This business idea can be considered in two directions:

1. As the main business of manufacturing finished products and molds by casting from: liquid:
   plastic;
2. silicone;
3. polyurethane;
4. transparent resins and other materials.
5. Mold making as an effective addition to other types of business in the area:
   construction;
6. Food Industry;
7. soap making

In the first and second cases, casting at home does not require large financial investments. You can start an injection molding business simply now.

Features of the use of various polymers

For plastic injection molding, different components are used that differ in physical parameters.

Low density polyethylene

LDPE is characterized by rapid melting. After cooling, it crystallizes and changes hardness. It is necessary to maintain a certain pressure and ensure the most uniform heating of the mold. Therefore, for cooling, water inlet is provided near the gating nozzles, and outlet is provided at a distant point. Filling with coolant is quick and the mold is well ventilated.

High Density Polyethylene

Compared to polyethylene NP, HDPE is characterized by better crystallization and a lower degree of fluidity in the molten form. Plastic molding of this type is widely practiced to produce products with thin walls, but at the same time sufficient structural rigidity is ensured.

Polypropylene

PP is characterized by crystallinity not exceeding 60%. The process is performed under reduced pressure and a fairly high plasticization temperature, which, depending on the type of material, can reach 280 ºC. The melt pressure is formed at a level of 140.0 MPa. The viscosity of the resulting mass is regulated by the shear rate and slightly depends on the temperature regime.

Polystyrene

PS is a material that, as a result of injection molding technology, is characterized by easy fluidity when molten. Allows the production of products that are characterized by structural rigidity and thin walls. The polymer is sensitive to overheating.

Impact-resistant polystyrene

UPS is a polymer that has a slightly higher viscosity than regular polystyrene and shrinks more when cooled. Used for thin-walled parts with increased resistance to mechanical stress.

Acrylonitrile butadione styrene plastic

ABS plastic is characterized by high viscosity in the molten state, is difficult to process and requires high pressure. It is used for the manufacture of parts with thin walls, but unlike, for example, polystyrene, ABS plastic has high rigidity and shock resistance.

Polymethyl methacrylate

PMMA makes it possible to obtain products of various shapes and configurations. It is characterized by low thermal stability and sensitivity to overheating with loss of physical parameters. Requires additional drying. The processing process requires precise temperature control. The peculiarity of the material is the formation of bubbles when injected into a cold mold, therefore the number of smooth transitions in it is minimized.

Polyvinyl chloride

PVC is widely used for injection molding because it is easy to process. The material is sensitive to temperature conditions and loses its properties when overheated. When in a molten state, it is characterized by instability and autocatalytic destruction, manifested in a different color shade. The color range can vary from ivory to cherry. To obtain all the properties of the polymer, it is necessary to carry out the plasticization process in a minimum time.

Polyamide

PA is a crystalline thermoplastic, characterized by hygroscopicity and good mass flow. When in a molten state, the volume increases by 15%. Due to the low thermal stability, the molding process for this type of plastic is completed in a minimum amount of time. Bubbles may form in the melt. The material requires additional time to dry thoroughly. The plasticization process is carried out at a pressure of 100 MPa. When filling injection molds, particle orientation is allowed.

Polycarbonate

PC is a heat-resistant polymer. It is characterized by high thermal stability and increased viscosity in the molten state, depending on the temperature. The mold is heated to a temperature of 100 ºС. Due to the increased hygroscopicity of the material, normal injection molding requires preheating in the cylinder of the injection molding machine and thorough drying.

Polyethylene terephthalate, polybutylene terephthalate and polyoxymethylene

PET, PBTF and POM are classified as polymers characterized by high thermal stability. The molding process for this type of plastic involves additional drying until the moisture content is reduced to 0.01%. In the molten state they have a medium viscosity, which decreases with decreasing temperature. To obtain thin-walled products, blowing with air is used.

Main types of defects and methods for eliminating them

During the injection molding process, due to violations of the technological process, excess melt temperature and other factors, defects occur that reduce the quality of the product:

• Incomplete filling of the mold (underfilling). Occurs due to insufficient volume of injected polymer. This situation is possible due to weak heating of the melt, low fluidity of the mass, clogging of the nozzle or distribution channels.
• Exceeding the volume of the mold (overflow) during the plastic molding process, causing the formation of burrs at the joint (burst). The defect occurs due to a malfunction of the dispenser or exceeding the permissible temperature of the molten polymer. The release of excess mass also occurs when the mold is not closed tightly enough.
• Joint seams are visible at the boundary of the soldering of individual parts of the part, which are characterized by low strength. Such joints are formed when the plasticization temperature is too low. The cause of the defect also lies in improper design or insufficient heating of the injection mold, which leads to premature cooling of the streams before they merge. As a result, complete welding cannot be achieved.
• Bubbles form on the surface of the product, and there are voids inside. Such a defect is the result of the presence of volatile components in the melt, characterized by increased gas release when overheated. The soft mass swells.
• Formation of shrinkage cavities (depressions) on the surface. The cause of the defect is increased shrinkage of the mass in case of overheating or insufficient volume of molten mass due to low pressure, as well as insufficient throughput of the nozzle. Such sinkholes appear when the injection mold is heated unevenly and has insufficient ventilation.
• Warping of manufactured parts. Defects occur when excessive internal tension occurs due to temperature unevenness of parts of the mold. Poor-quality products are also obtained if the time required to hold the mass for complete hardening is not observed.
• Cracks on the surface. They occur due to residual stress or in case of strong adhesion of the liquid mass to the walls.
• Surface defects of parts, manifested by scratches and chips. Defects occur in the event of careless handling of finished products or poorly designed molds.
• Patterns that resemble frosty patterns on glass appear due to excessive amounts of moisture in the injected molten mass. A deficiency occurs when the drying and ventilation process of the mold is disrupted.
• If there is moisture in the polymer material in excess of the established norm, delamination of the structure occurs. The defect also occurs when there are frozen sprues that are not aligned with the main mass.
• Uneven (different) tone color of the product. The reason is the use of a thermally unstable dye and overheating of the molten mass.
• The received product does not meet the required dimensions, exceeding the standard tolerance. It occurs due to severe shrinkage of the plastic during hardening or a poorly made mold.

Polyurethane forms for construction

Along with plastic products, injection molds can be produced. The use of injection molds in construction is now very popular. It is possible to produce compounds for the production of building materials. They are durable and do not require treatment with special release lubricants during manufacturing. After all, concrete is absolutely neutral to polyurethane. For example, liquid polyurethane compounds make it possible to produce molds for filling:

• concrete decorative products (tiles, fences, etc.);
• plaster elements of interior decoration (balusters, stucco, etc.);
• liquid plastic when creating a wide variety of products (souvenirs, toys, figurines, etc.).

Examples of defects and solutions

High-quality plastic injection molding that meets standard requirements is ensured by using a technically sound machine, strictly following technological steps and using high-quality raw materials. The table lists the types of defects and actions to prevent them.

Injection molding technology, implemented on modern equipment in compliance with process requirements and the use of high-quality raw materials, allows us to produce large quantities of high-quality products that are in demand in various industries and domestic conditions. By choosing the optimal plasticization method, it is possible to establish cost-effective production of parts of any complexity.